A scientist familiar with First Solar’s earlier efforts in CIGS makes the case for the CdTe pioneer to return to the technology.
From pv magazine USA
An earlier article assessed the significant capital efficiency and carbon advantages of thin-film PV over c-Si. We’ve also explored the malaise plaguing thin-film PV manufacturing. Although the manufacturing malaise endures, there have been significant developments worth analyzing.
At approximately 33%, the theoretical efficiency limits for crystalline silicon (c-Si), cadmium telluride (CdTe) and copper indium gallium selenide (CIGS) photovoltaic materials are roughly identical. And given the extensive history of c-Si research and manufacturing, it comes at no surprise that silicon’s record device efficiency of 26.7% has narrowed the gap between theory and use.
The official CdTe record device efficiency of 21% for a 1 cm2 R&D cell from First Solar’s lab – as documented in the solar cell efficiency tables published in Progress in Photovoltaics – has not improved since v45 of the tables were published in October 2014. Subsequently, First Solar was able to leverage the acquisition of the GE IP for a “notable exception,” a R&D device of just 0.3 cm2 at 21.5% (v46 of the efficiency tables, data as of May 2015) and one year later in May of 2016 (v48) demonstrated a “notable exception” at 22.1% (0.48 cm2).
In contrast to the six-year stagnation at the ≥ 1 cm2 device level for CdTe, CIGS has made continuous progress, currently at 23.35% through a two-step processing by Solar Frontier.
The significance of laboratory records demonstrates a technology’s potential, but ultimately the performance of PV modules and associated manufacturing costs determine financial viability. Due to scaling effects – mainly series resistance losses –the absolute delta between record device efficiency and average module efficiency is at the order of 3%, the gap between record R&D devices and champion modules tends to be ≈ 2%. With average Series 6 modules and a champion at ≈ 18% and 19%, respectively, First Solar’s CdTe fits the bill – similar to c-Si.
Monolithically interconnected CIGS on glass, on the other hand, suffers from much wider gaps, at ≈ 8.5% and ≈ 4%, respectively, the deltas are approximately 2x larger than for CdTe and c-Si. This is due to a lack of manufacturing execution expertise, and difficulties scaling a two-step CIGS process to larger areas.
At this point it may appear that trouble lies ahead for thin-film PV. The efficiency stagnation of First Solar’s CdTe technology is worrisome.
To add to this, during the Q2’20 earnings call, First Solar reported a delay of its CuRe efforts – replacing Cu via Group V doping (As, Sb). First results are now expected for H2’21 and fleet wide implementation during 2022.
No public announcements have been made as to the efforts towards bifacial modules. Since the back contact is the Achilles’ heel of CdTe, no rapid breakthrough towards a transparent back contact is to be expected. Unfortunately, the latter is also a prerequisite for other R&D efforts undertaken by First Solar, namely c-Si/CdTe and CdTe/perovskite tandem devices.
While there are further economic and technical hurdles for tandem technologies, in particular with perovskites, a bifacial CdTe technology would be highly desirable for First Solar for two reasons: First Solar’s dependence on the U.S. utility scale market, and the uncertain future of the section 201 protections including the exemption for bifacial c-Si modules. As with c-Si, a bifacial CdTe module would have no value in rooftop applications.
Back to CIGS
First Solar has concluded that co-evaporation of CIGS is the superior thin-film technology. While it has gambled away eight valuable years, the company not only has a treasure trove of data from its earlier program, but has acquired key IP assets from a recently defunct Silicon Valley CIGS company and can leverage an extremely capable equipment vendor base.
In light of all this, it makes perfect sense for First Solar to dedicate resources towards co-evaporated CIGS as a parallel technology. One would hope that this time around First Solar sees it through and does not stop prematurely as in 2011.
Co-evaporation of CIGS is not a technical risk – the roadmap and supply chain exist, and the high degree of automation reduces manufacturing location related cost sensitivity. Now would be the time to build a team and enable a ‘Second Solar’ made in the United States rivaling First Solar.
Markus Beck is a thin-film solar expert and a business and technology consultant who has served as the chief technologist of Siva Power and chief scientist of the CIGS effort at First Solar.