Inverted blade-coated perovskite cell with 23.2% efficiency

A US research team has improved the efficiency of a blade-coated perovskite cell with a p-i-n structure by reducing iodine-induced charge traps in the films. They used the cells to fabricate a mini module with an efficiency of 18.2%.

Scientists from the University of North Carolina have developed a perovskite solar cell with an efficiency of 23.2% by adding benzylhydrazine hydrochloride (BHC) as an iodine (I) reductant agent in precursor solutions such as methylammonium iodide (MAI) and formamidinium iodide (FAI).

“Preventing the degradation of perovskite precursor solutions is equally important compared to post-fabrication device encapsulation, because large-area perovskite modules are generally manufactured in air and perovskite precursor inks are generally prepared in large quantity and stored for days or months,” the scientists said.

They said that one of the most common issues with precursor materials is that that iodine (I) ions are oxidized into elemental diatomic iodine (I2) during storage. This deteriorates the overall performance of the affected perovskite solar cell, they noted. The group used a low-cost BHC as a reductant, which reduced I2 back to I in aged precursor solutions.

“In addition, the BHC residual in perovskite solid films can reduce the I2 generated during light soaking that induces the shallow charge traps and accelerates the decomposition of perovskite materials,” they said.

Through this process, the academics were able to fabricate an inverted blade-coated p-i-n perovskite cell with the aforementioned efficiency, which was certified by the US Department of Energy’s National Renewable Energy Laboratory (NREL). It also exhibited operational stability, with almost zero degradation after 1,000 hours of operation at maximum power point (MPP), using a perovskite composition that does not contain cesium. The cell also exhibited an open-circuit voltage of 1.17 V, a short circuit current of 24.0 mA cm2, and a fill factor of 0.829.

Popular content

“All these results demonstrate the effectiveness of BHC in restoring precursor solutions and reducing film defects, accounting for the suppressed charge recombination and thus enhanced device efficiency,” the researchers said.

They then used the cells to produce perovskite mini-modules with an 18.5% efficiency level, as well as an open-circuit voltage of 11.7 V, a short-circuit current of 73.20 mA, and a fill factor of 0.773. They presented their findings in “Iodine reduction for reproducible and high-performance perovskite solar cells and modules,” which was recently published in Science Advances.